| About |
|---|
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Features | Good Electrical Properties,weathering resistance,Good heat resistance and aging,Good Clarity |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.872 | g/cm³ | ASTM D792 |
| Melt Index | |||
| 190℃，2.16kg | 4.8 | g/10min | ASTM D1238 |
| Mooney viscosity | |||
| ML1+4,121℃ | 8 | MU | ASTM D1646 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| 100% cutting Secant | 2.3 | MPa | ASTM D638 |
| Tensile Strength | |||
| Broken BRK | 5.7 | MPa | ASTM D638 |
| Elongation at Break | 1100 | % | ASTM D638 |
| Flexural Modulus | |||
| 1% cutting Second | 10.9 | MPa | ASTM D790 |
| 2% cutting Second | 10.8 | MPa | ASTM D790 |
| Tear strength | 37.1 | kN/m | ASTM D624 |
| Shore hardness | |||
| 66 | Shore A | ASTM D2240 | |
| 17 | Shore D | ASTM D2240 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass Transition Temperature | -53 | ℃ | Internal Method |
| Vicat Softening Temperature | 37 | ℃ | ASTM D1525 |
| Melting temperature | 59 | ℃ | Internal Method |
| Peak Crystallization Temperature (DSC) | 44 | ℃ | Internal Method |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | >1E15 | ohms·cm | Internal Method |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |