| CYCOLOY CE3510 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a grade that can be injection molded or extruded into sheet for secondary thermoforming operations. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 flame rating. CYCOLOY CE3510 resin is a general purpose resin that is an excellent candidate for a wide variety of applications including cable channels and is verified non-halogen by the DIN VDE 0472/815 standard.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Halogen free,Flame Characteristics,High Heat Resistance,V-2,V-0 |
| Availabilitys | Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.20 | g/cm³ | ASTM D792 |
| — | 1.21 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 260℃，5 kg | 8.00 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2680 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 64.0 | MPa | ASTM D638 |
| yield | 65.0 | MPa | ISO 527-2/50 |
| fracture | 49.0 | MPa | ASTM D638 |
| fracture | 50.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 4.3 | % | ASTM D638 |
| yield | 4.6 | % | ISO 527-2/50 |
| fracture | 35 | % | ASTM D638 |
| fracture | > 50 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2610 | MPa | ASTM D790 |
| — | 2480 | MPa | ISO 178 |
| bending strength | |||
| — | 95.0 | MPa | ISO 178 |
| Yield, 50 mm span | 95.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 14 14 | kJ/m² | |
| 23℃ | 45 45 | kJ/m² | |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 无断裂 无断裂 | ||
| 23℃ | 无断裂 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| -30℃ | 110 | J/m | ASTM D256 |
| 23℃ | 660 | J/m | ASTM D256 |
| -30℃ | 12 | kJ/m² | ISO 180-1A |
| 0℃ | 14 | kJ/m² | ISO 180-1A |
| 23℃ | 20 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 无断裂 无断裂 | ||
| 23℃ | 无断裂 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 111 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span | 111 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.2 mm | 100 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 100 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| B50 | 116 | ℃ | ISO 306 |
| B120 | 118 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 75℃ | Pass | IEC 60695-10-2 | |
| Relative temperature index | 90.0 | ℃ | UL 746 |
| Electrical performance | 90.0 | ℃ | UL 746 |
| Impact mechanical performance | 90.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | IEC 60243-1 | ||
| 0.8 mm in oil | 44 | kV/mm | |
| 1.6 mm in oil | 27 | kV/mm | |
| 3.2 mm in oil | 18 | kV/mm | |
| Compared to the leakage tracing index | PLC 3 PLC 3 | UL 746 | |
| Compared to the leakage tracing index | 225 225 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-2 | ||
| 1.50 mm | V-0 | ||
| Glowing wire flammability index | |||
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1 mm | 825 | ℃ | |
| 1.5 mm | 825 | ℃ | |
| 3 mm | 825 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80.0 to 85.0 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel temperature | 60.0 to 80.0 | °C | |
| Barrel 1 zone temperature | 235 to 260 | °C | |
| Barrel 2 zone temperature | 240 to 265 | °C | |
| Barrel 3 zone temperature | 245 to 270 | °C | |
| Barrel 4 zone temperature | 245 to 270 | °C | |
| Connector temperature | 245 to 270 | °C | |
| Melt temperature | 230 to 270 | °C | |
| Nozzle temperature | 235 to 260 | °C | |
| Calibration temperature, first time | 60.0 to 80.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. 120*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |