| About |
|---|
| This grade meets UL94, V-0 Flammability rating without Chlorine and Bromine*. It has good balance of mechanical properties and flow-ability as well as other V-0 grades containing Bromine Flame Retardant (BFR). *’Halogen free’ follows the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm.&& |
| Product Description | |
|---|---|
| Supplier | Kuraray |
| Generic | PA 9T |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Food contact compliance,Good melt strength,Ultra high molecular weight,Copolymer,Hexene copolymers,High ESCR,V-0 |
| Availabilitys | Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.53 | g/cm³ | |
| Shrinkage rate | |||
| MD：1.0 mm | 0.040 | % | |
| TD：1.00 mm | 0.50 | % | |
| Water absorption rate | |||
| Equilibrium, 40 ℃, 95% RH | 0.80 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 165 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | 13000 | MPa | ASTM D790 |
| bending strength | 224 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 100 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 285 | ℃ | ASTM D648 |
| Glass transition temperature | 125 | ℃ | |
| Melting temperature | 306 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | 30 | kV/mm | ASTM D149 |
| Compared to the leakage tracing index | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Rod flow length | |||
| 320℃，500.0 µm | 5.50 | cm | |
| Weld Elongation | 0.40 | % | ASTM D638 |
| Weld Strength | 38.0 | MPa | ASTM D638 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 96 hrs |
| 3. 750kgf |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |