| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Bromine free,non-phosphorus ,weathering resistance,Flame Characteristics |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.2 kg | 3.0 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 3.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| vertical | 0.5-0.7 | % | |
| flow | 0.5-0.7 | % | |
| Water Absorption | |||
| saturated，23℃ | 0.24 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527 |
| Tensile Strength | |||
| yld | 64 | MPa | ISO 527-2 |
| Tensile Strain | |||
| yld | 5.8 | % | ISO 527 |
| brk | 56 | % | ISO 527 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Strength | 100 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy notched Impact strength | 58 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact strength | NB | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| HDT | |||
| 0.45 MPa，unannealed | 136 | ℃ | ISO 75-1/-2 |
| 1.80 MPa，unannealed | 125 | ℃ | ISO 75-1/-2 |
| Coeff.of linear therm expansion | |||
| flow | 6.5E-5 | cm/cm/℃ | ISO 11359-2 |
| vertical | 6.6E-5 | cm/cm/℃ | ISO 11359-2 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface Resistivity | 6E15 | ohms | IEC 60093 |
| Volume Resistivity | 3E16 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 3 | PLC Code | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 120 | ℃ | |
| Drying Time | 4-8 | hr | |
| Rear Temperature -Zone 1 | 280-310 | ℃ | |
| Middle Temperature -Zone 2 | 280-310 | ℃ | |
| Front Temperature -Zone 3 | 280-310 | ℃ | |
| Nozzle Temperature | 280-310 | ℃ | |
| Mold Temperature | 70-100 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |