| PA66 engineering plastic is one of the engineering plastic series produced by South Asia Plastics Industry Co., Ltd. It is produced through a mixing process and has superior mechanical properties, high rigidity, impact resistance, thermal aging resistance, and chemical properties. Moreover, due to its good processability, self lubrication, wear resistance, and self extinguishing properties, it can be applied in the information, electronics, motor, and automotive industries. South Asia FR-PA666110 is a specification with excellent toughness, impact resistance, and high crystallinity. It is used in high toughness and impact resistant parts such as tennis racket protectors and sports equipment. |
| Product Description | |
|---|---|
| Supplier | Nan Ya |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | processability,Mechanical property,low-temperature impact resistance,Good wear resistance,Good heat aging resistance,Self-lubricating,high-rigidity |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile Strength | 800 | kg/cm² | ASTM D638 |
| Tensile Elongation | — | % | ASTM D638 |
| Flexural Strength | 1050 | kg/cm² | ASTM D790 |
| Flexural Modulus | 25000 | kg/cm² | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | 6.5 | Kg-cm/cm | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| HDT | |||
| 1.80 MPa | 75 | ℃ | ASTM D648 |
| Relative Temp Index(RTI) | |||
| electrical | |||
| 0.75 mm | 130 | ℃ | UL746B |
| 3.0 mm | 130 | ℃ | UL746B |
| impact | |||
| 0.75 mm | 80 | ℃ | UL746B |
| 3.0 mm | 85 | ℃ | UL746B |
| strength | |||
| 0.75 mm | 85 | ℃ | UL746B |
| 3.0 mm | 85 | ℃ | UL746B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 0.75 mm | HB | UL 94 | |
| Glow Wire Flammability Index(GWFI) | |||
| 3.0 mm | — | ℃ | IEC 60695-2-12 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistivity | 1E14 | ohm·cm | ASTM D257 |
| insulation Strength | 22 | kV/mm | ASTM D-149 |
| Comparative Tracking Index | — | V | ASTM D36381 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Specific Gravity | 1.14 | ASTM D792 | |
| Melt Index | 30 | g/10min | ASTM D1238 |
| Molding Shrinkage | |||
| MD | 1.3-1.6 | % | |
| TD | 1.3-1.7 | % |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 80 | ℃ | |
| Drying Time | 4 | hr | |
| Rear Temperature -Zone 1 | 270 | ℃ | |
| Middle Temperature -Zone 2 | 275 | ℃ | |
| Front Temperature -Zone 3 | 275 | ℃ | |
| Nozzle Temperature | 280 | ℃ | |
| Mold Temperature | 80-100 | ℃ | |
| Injection pressure | 500-900 | MPa | |
| Screw Speed | 120 | kg/cm² | |
| Injection speed | 快速 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |