| About |
|---|
| KEPSTAN® 8010G40 resin is aglass fiber reinforced compound, based on the 6000 series of KEPSTAN® resins. This series offers the highest glass transition temperature and the highest crystallinity, leading to the best tensile and compression strengths among the different series of KEPSTAN® PEKK copolymers.KEPSTAN® 8010G40 resin is a low flow grade, suitable for extrusion, compression and injection molding. |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Material Status | Commercial: Negative |
| Availabilitys | Asia Pacific,North America,Latin America,Europe,Africa & Middle East |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Volume Rate | |||
| 380℃，5kg | 7 | cm³/10min | ISO 1133 |
| Density | 1520 | kg/m³ | ISO 1183 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion Molded | Nominal value | Unit | Test method |
| Injection Molding | Nominal value | Unit | Test method |
| Barrel – Zone 1 Temperature | 355 | ℃ | |
| Barrel – Zone 2 Temperature | 370 | ℃ | |
| Barrel – Zone 3 Temperature | 385 | ℃ | |
| Barrel – Zone 4 Temperature | 385 | ℃ | |
| Die Temperature | 370 | ℃ | |
| Drying Temperature | 150 | ℃ | |
| Drying Time | 3-4 | hr | |
| Processing temperature | 375-385 | ℃ | |
| Rear Temperature -Zone 1 | 350 | ℃ | |
| Middle Temperature -Zone 2 | 375 | ℃ | |
| Front Temperature -Zone 3 | 375 | ℃ | |
| Nozzle Temperature | 385 | ℃ | |
| Mold Temperature | 230-240 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |