| EMERGE™ PC 8702 Advanced Resin is an ignition-resistant, 20% glass reinforced, polycarbonate resin. This resin contains no bromine, chlorine, or phosphate additives. The resin is designed to meet the German norm DIN VDE-0472/Part 815 (1989) on halogens. It is a medium flow PC resin with a mold release system, intended for injection molding applications. Applications: Information technology equipment Electrical parts Other structural/internal parts&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Moderate liquidity,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.20 to 0.40 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 3.20 mm, injection molded | 4000 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 3.20 mm, injection molded | 100 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm, injection molded | 4.0 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 5380 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 120 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 110 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 145 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 140 | ℃ | ASTM D648 |
| 1.8 MPa, annealed | 143 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 3.0E+14 | ohms | ASTM D257 |
| Volume resistivity | |||
| 1.80 mm | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1.6 mm | 27 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1.60 mm，1 MHz | 3.10 | ASTM D150 | |
| Compared to the leakage tracing index | |||
| 3.00 mm | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 288 to 316 | °C | |
| Mold temperature | 79 to 116 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |