| About |
|---|
| 30% Glass Reinforced, Halogen free and free of red phosphorous&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Low to no phosphorus content |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.44 | g/cm³ | ISO 1183 |
| Saturation, 23 ℃ | 4.3 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 1.6 | % | ISO 62 |
| Shrinkage rate | |||
| MD | 0.8 | % | ISO 294-4 |
| TD | 0.2 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 150 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 208 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy impact strength | |||
| 23℃ | |||
| Gap | 9 | kJ/m² | ISO 179/1eA |
| No gap | 63 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 245 | ℃ | ISO 75-2/A |
| Melting temperature | 260 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| desiccation | 36 | kV/mm | IEC 60243-1 |
| After adjustment | 32 | kV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.40 mm | V-0 | IEC 60695-11-10, -20 | |
| 1.50 mm | V-0 | IEC 60695-11-10, -20 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Injection speed | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0~8.0 | hr | |
| Barrel rear temperature | 260~280 | °C | |
| Barrel middle temperature | 270~290 | °C | |
| Barrel front temperature | 265~275 | °C | |
| Nozzle temperature | 260~265 | °C | |
| Processing (melt) temperature | 265~285 | °C | |
| Mold temperature | 50~ 80 | °C | |
| Back pressure | 3.00~10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |