PRIMACOR™ 5980I

About
Low heat seal temperature, high hot tack High gloss, excellent clarity Excellent grease and oil resistance, water hold-out and excellent product resistance for flexible packaging applications Complies with: U.S. FDA 21 CFR 177.1310(a)(2) Consult the regulations for complete details. PRIMACOR™ 5980I is an ethylene acrylic acid copolymer with excellent adhesion to metallic, cellulosic, glass and other polar substrates. In dispersion form, it can be used effectively as a foil primer or laminating adhesive for polyethylene and metallized substrates. Applications: Adhesives Laminations Foil priming Heat sealing Nonwoven binding Metal/paper coating Outstanding Properties: Dispersible in aqueous amines and alkali “Clean” dispersion requires no salts, surfactants or solvents Dispersions use existing waterbourne application equipment High hot tack Low odor&&

About

Low heat seal temperature, high hot tack High gloss, excellent clarity Excellent grease and oil resistance, water hold-out and excellent product resistance for flexible packaging applications Complies with: U.S. FDA 21 CFR 177.1310(a)(2) Consult the regulations for complete details. PRIMACOR™ 5980I is an ethylene acrylic acid copolymer with excellent adhesion to metallic, cellulosic, glass and other polar substrates. In dispersion form, it can be used effectively as a foil primer or laminating adhesive for polyethylene and metallized substrates. Applications: Adhesives Laminations Foil priming Heat sealing Nonwoven binding Metal/paper coating Outstanding Properties: Dispersible in aqueous amines and alkali “Clean” dispersion requires no salts, surfactants or solvents Dispersions use existing waterbourne application equipment High hot tack Low odor&&

Product Description
Supplier	DOW
Generic	EAA
Material Status	Commercial: Negative
Availabilitys	North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.958	g/cm³	ASTM D792 , ISO 1183
Melt Flow Rate			ASTM D1238 , ISO 1133
125℃，2.16kg	14	g/10min	ASTM D1238，ISO 1133
190℃，2.16kg	300	g/10min	ASTM D1238，ISO 1133
Co monomer content	20.5	%	Internal Method

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	42.2	℃	ASTM D1525 , ISO 306
Melting temperature
DSC	77.2	℃	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	50		ASTM D2240 , ISO 868
Tensile modulus
2% cut, molded	33.1	MPa	ASTM D638 , ISO 527-2
tensile strength
Fracture, molded	9.65	MPa	ASTM D638 , ISO 527-2
Tensile strain
Fracture, molded	390	%	ASTM D638 , ISO 527-2

Notes
1. Typical properties: these are not to be construed as specifications.
2. As measured at the time of production.
3. Melt Index values are correlated from Melt Flow Rate (ASTM D 1238 conditions of 125°C/2.16kg).
4. Comonomer content measured by a proprietary method that has equivalent accuracy as compared to ASTM D 4094.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.