| About |
|---|
| PARYLS® PPSU F1350 pellets are supplied in cartons lining aluminum foil bag, which can be stored indefinitely, provided the packaging remains undamaged. PARYLS® PPSU F1350 pellets absorb moisture very rapidly. Therefore, the pellets need to be dried at least 6h at 180 °C in a vacuum or dry air drier prior to processing.&& |
| Product Description | |
|---|---|
| Supplier | Youju |
| Generic | PPSU |
| Material Status | Commercial: Active |
| Features | Low Viscosity,No BPA,V-0 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.29 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 365℃，5.0kg | 28 to 38 | g/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 , ISO 2577 | ||
| TD | 1.0 | % | ISO 294-4，ISO 2577 |
| MD | 0.90 | % | ISO 294-4，ISO 2577 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.35 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2270 | MPa | ISO 527-2 |
| tensile strength | 70.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 7.8 | % | ISO 527-2 |
| Bending modulus | 2400 | MPa | ISO 178 |
| bending strength | 105 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 68 | kJ/m² | ISO 180/A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 196 | ℃ | ISO 75-2/A |
| Glass transition temperature | 220 | ℃ | ISO 11357-2 , DSC |
| Linear coefficient of thermal expansion | |||
| MD：23℃ | 5.5E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 44 | kV/mm | IEC 60243-1 |
| Dielectric constant | IEC 60250 | ||
| 100 Hz | 3.80 | IEC 60250 | |
| 1 MHz | 3.70 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 1.5E-3 | IEC 60250 | |
| 1 MHz | 8.6E-3 | IEC 60250 | |
| Compared to the leakage tracing index | 150 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 180 | °C | |
| Drying time | 6.0 | hr | |
| Processing (melt) temperature | 350 to 390 | °C | |
| Mold temperature | 140 to 180 | °C | |
| Drying temperature | 180 | °C | |
| Drying time | 6.0 | hr | |
| Melt temperature | 350 to 390 | °C | |
| Nozzle temperature | 140 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 3. 100V |
| 4. K20/K20, (60*60*1 mm³) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |