| About |
|---|
| SABIC® HDPE B5403 is typically used for blow moulding UN certified Tight Head drums, from 25 up to 220 liter. This food approved grade combines good processing performance with good stress crack resistance, stiffness and impact performance. This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High impact resistance,Food contact compliance,High density,High ESCR |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.954 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，21.6kg | 2.7 | g/10min | ISO 1133 |
| 190℃，5.0kg | 0.10 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30 ℃, molded | 60 | kJ/m² | ISO 180-A |
| 23 ℃, molded | 72 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 78.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 129 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 132 | ℃ | ISO 11357-3 |
| Enthalpy Change | 195 | J/g | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 61 | ISO 868 | |
| Tensile modulus | |||
| 2 mm, molded into shape | 1250 | MPa | ISO 527-2/1BA/50 |
| tensile strength | ISO 527-2/1BA/50 | ||
| Yield, 2 mm, molded | 26.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2 mm, molded | 39.0 | MPa | ISO 527-2/1BA/50 |
| Tensile strain | ISO 527-2/1BA/50 | ||
| Yield, 2 mm, molded | 14 | % | ISO 527-2/1BA/50 |
| Fracture, 2 mm, molded | > 1000 | % | ISO 527-2/1BA/50 |
| Bending modulus | |||
| 2 mm, molded into shape | 1250 | MPa | ISO 178 |
| bending strength | |||
| 2 mm, molded into shape | 27.0 | MPa | ISO 178 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| Strain Hardening – Gp | 23.0 | MPa | ISO 18488 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |