SECCO GPPS-123

About
GPPS123 retains high fluidity and good mould release and allows excellent transparency and gloss.&&

Product Description
Supplier	SECCO
Generic	PS (GPPS)
Material Status	Commercial: Active
Features	Good Clarity,Good surface appearance,High liquidity,Good stripping performance,HB
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.04	g/cm³	ISO 1183
Melt Flow Rate
200℃，5.0kg	8.0	g/10min	ISO 1133
Shrinkage rate	0.40 to 0.60	%	ISO 294-4
Water absorption rate
Saturation, 23 ℃	< 0.10	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	47.0	MPa	ISO 527-2/50
Tensile strain
fracture	2.0	%	ISO 527-2/50
Bending modulus	3100	MPa	ISO 178
bending strength	75.0	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Unnotch Impact strength
23℃	9.0	kJ/m²	ISO 179/1eU

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	73.0	℃	ISO 75-2/A
Vicat Softening Temp
B50	91.0	℃	ISO 306

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

optical performance	Nominal value	Unit	Test method
Transmittance	90.0	%	ASTM D1003

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.