| About |
|---|
| Flame Retardant (halogen- phosphorous-free) Special Features: Phosphorous free EcoPaXX® is our bio-based, high-performance polyamide (PA410) that offers outstanding performance across the board, while being made mainly from tropical castor beans which don€™t compete with the food chain. EcoPaXX® belongs to the family of long-chain polyamides, which offer exceptional performance in the most demanding of environments. That includes excellent chemical resistance, low moisture absorption, combined with a very high melting point (highest of all bio-plastics) and high crystallization rate (typical for engineering plastics like PA66 and PA46). And€¦ EcoPaXX® is certified 100% carbon neutral from cradle to gate. That means the amount of carbon dioxide emitted during the production of EcoPaXX is offset by the amount absorbed in plant growth, and in particular by thericcinus communis €” the tropical castor bean plant that makes up some 70% of EcoPaXX. |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 410 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Low to no phosphorus content |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | |||
| TD | 0.90 | % | |
| MD | 1.1 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.7 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3600 | MPa | |
| tensile strength | |||
| fracture | 75.0 | MPa | |
| Tensile strain | |||
| yield | 4.0 | % | |
| fracture | 5.0 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.2 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 80 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 190 | ℃ | |
| 1.8 MPa, unannealed | 110 | ℃ | |
| Melting temperature | 250 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | |
| Dielectric strength | 32 | kV/mm | |
| Compared to the leakage tracing index | — | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 0.40 mm | V-0 | ||
| 1.5 mm | V-0 | ||
| Glowing wire flammability index | |||
| 0.75 mm | 960 | ℃ | |
| Igniting temperature of the hot wire | |||
| 0.75 mm | 960 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 255 to 265 | °C | |
| Barrel middle temperature | 260 to 270 | °C | |
| Barrel front temperature | 260 to 270 | °C | |
| Nozzle temperature | 260 to 275 | °C | |
| Processing (melt) temperature | 260 to 280 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Injection speed | 中等偏快 | ||
| Back pressure | 3.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |