| PC+Polyester, UV Stabilized, Transparent&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC + Polyester |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,V-2 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 265℃，2.16kg | 15 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 265℃，2.16 kg | 15.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.40 to 0.60 | % | Internal Method |
| MD：3.2 mm | 0.50 to 0.80 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.050 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 10 seconds | 74 | ASTM D2240 | |
| Tensile modulus | 1520 | MPa | ASTM D638 |
| Tensile modulus | 1600 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 54.0 | MPa | ISO 527-2/50 |
| fracture | 46.0 | MPa | ASTM D638 |
| yield | 47.0 | MPa | ASTM D638 |
| yield | 55.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 150 | % | ASTM D638 |
| fracture | > 200 | % | ISO 527-2/50 |
| yield | 5.0 | % | ASTM D638 |
| yield | > 5.0 | % | ISO 527-2/50 |
| Bending modulus | 1700 | MPa | ISO 178 |
| 50 mm span | 1680 | MPa | ASTM D790 |
| bending strength | 78.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 71.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 73 | J/m | ASTM D256 |
| 23℃ | 1100 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 7.0 | kJ/m² | ISO 180-1A |
| -10℃ | 5.0 | kJ/m² | ISO 180-1A |
| 23℃ | 8.0 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 95.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 75.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 79.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 80.0 | ℃ | ISO 75-2/Ae |
| 1.8 MPa, unannealed, 64 mm span | 78.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | 91.0 | ℃ | ASTM D1525 11 |
| B120 | 96.0 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 85℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 1.1E-4 | 1/℃ | ASTM E831 |
| TD | ISO 11359-2 | ||
| MD：-40~40℃ | 1.1E-4 | 1/℃ | ASTM E831 |
| MD | ISO 11359-2 | ||
| -40 to 40 ℃ | 1.1E-4 | cm/cm/℃ | ISO 11359-2 |
| 23 to 60 ℃ | 9.0E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 to 40 ℃ | 1.1E-4 | cm/cm/℃ | ISO 11359-2 |
| 23 to 60 ℃ | 9.0E-5 | cm/cm/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.23 | W/m/K | ISO 8302 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Compared to the leakage tracing index | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | V-2 | UL 94 | |
| Glowing wire flammability index | |||
| 1.0 mm | 750 | ℃ | IEC 60695-2-12 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.539 | ISO 489 | |
| Transmittance | |||
| 2540 µm | 88.0 | % | ASTM D1003 |
| Haze | |||
| 2540 µm | 1.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 66 to 77 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 80 | % | |
| Barrel rear temperature | 238 to 249 | °C | |
| Barrel middle temperature | 238 to 260 | °C | |
| Barrel front temperature | 243 to 266 | °C | |
| Nozzle temperature | 243 to 266 | °C | |
| Processing (melt) temperature | 243 to 266 | °C | |
| Mold temperature | 43 to 60 | °C | |
| Back pressure | 0.172 to 0.517 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.013 to 0.020 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Break |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. 120*10*4 mm |
| 10. Rate A (50°C/h), Loading 2 (50 N) |
| 11. Approximate Maximum |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |