| About |
|---|
| PA66阻燃注塑料，不含卤素和红磷。采用25%玻纤加固。适合制造要求具备阻燃特性的部件，也适合要求具备中等刚度的部件，还适合要求具备良好力学阻力的部件，另外还适合要求具备良好的电气绝缘特性，并且根据UL-94评级为V-0的部件。 |
| Product Description | |
|---|---|
| Supplier | Radici |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Electrical Properties,Halogen free,Flame Characteristics,Low to no phosphorus content,Insulation |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | |
| Shrinkage rate | |||
| TD | 1.0 | % | |
| MD | 0.40 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃, 2.00 mm | 5.5 | % | |
| Equilibrium, 23 ℃, 2.00 mm | 1.3 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8700 | MPa | |
| tensile strength | |||
| fracture | 135 | MPa | |
| Tensile strain | |||
| fracture | 2.9 | % | |
| Bending modulus | 8500 | MPa | |
| bending strength | 210 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 65 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 240 | ℃ | |
| Vicat Softening Temp | 245 | ℃ | |
| Melting temperature | 260 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+12 | ohms | |
| Volume resistivity | 1.0E+15 | ohms·cm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | ||
| Burning rate | |||
| 3.0 mm | 0.0 | mm/min | |
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | |
| 2.0 mm | 960 | ℃ | |
| Igniting temperature of the hot wire | |||
| 1 mm | 725 | ℃ | |
| 2 mm | 775 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 80 | °C | |
| Drying time – hot air dryer | 2.0 to 4.0 | hr | |
| Dew Point – Hot Air Dryer | < -20 | °C | |
| Recommended maximum moisture content | 0.10 | % | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Injection speed | 中等偏快 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |