| About |
|---|
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,Good liquidity,Heat Resistance, Good,Good coloring |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 220℃，10 kg | 19.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.22 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 8.0 | kJ/m² | ISO 179 |
| 23℃ | 22 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 100 | kJ/m² | ISO 179 |
| 23℃ | 180 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| -30℃ | 8.0 | kJ/m² | ISO 180-A |
| 23℃ | 26 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 94.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, annealed | 99.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 105 | ℃ | ISO 306/A50 |
| B50 | 96.0 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 0.8E-4 to 1.1E-4 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.17 | W/m/K | DIN 52612 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric constant | |||
| 1.00 mm，1 MHz | 2.80 | ASTM D150 | |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 2.90 | IEC 60250 | |
| 1 MHz | 2.80 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 4.8E-3 | IEC 60250 | |
| 1 MHz | 7.9E-3 | IEC 60250 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2300 | MPa | ISO 527 |
| Tensile stress | |||
| Yield, 23 ℃ | 45.0 | MPa | ISO 527 |
| Tensile strain | |||
| Yield, 23 ℃ | 2.6 | % | ISO 527 |
| Nominal tensile fracture strain | |||
| 23℃ | 10 | % | ISO 527 |
| Bending modulus | 2300 | MPa | ISO 527 |
| bending strength | 65.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 103 | ASTM D785 | |
| Ball hardness | 97.0 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Melting temperature | 220-260 | ℃ | |
| Mold temperature | 30-80 | ℃ | |
| Injection speed | 200 | mm/s | |
| drying temperature | 80 | ℃ | |
| Drying time | 2-4 | hr | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |