| About |
|---|
| Kingfa PA66-RPG25 is a Polyamide 66 (Nylon 66) material filled with 25% glass fiber. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa PA66-RPG25 are: Flame Rated Flame Retardant Halogen Free Heat Resistant High Strength Typical application of Kingfa PA66-RPG25: Electrical/Electronic Applications&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Electrical Properties,Halogen free,Low to No Fogging,Flame Characteristics,High Heat Resistance |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.80 to 1.1 | % | |
| MD | 0.30 to 0.50 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.6 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 8.5 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 250 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 235 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 19 | kV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ISO 2039-2 | |
| tensile strength | 145 | MPa | ISO 527-2/10 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2/10 |
| Bending modulus | 7500 | MPa | ISO 178 |
| bending strength | 210 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 110 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 250 to 265 | °C | |
| Barrel middle temperature | 265 to 275 | °C | |
| Barrel front temperature | 270 to 280 | °C | |
| Processing (melt) temperature | 260 to 290 | °C | |
| Mold temperature | 70 to 90 | °C | |
| Injection speed | 中等偏快 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |