| COSMOPLENE FL632L is Polypropylene Terpolymer product designed for cast PP with low heat seal temperature, high transparency and roll mark free at high speed. COSMOPLENE FL7632L is suitable for heat sealing layer for dry lamination with BOPP film. FL7632L contains slip and anti-blocking agents.&& |
| Product Description | |
|---|---|
| Supplier | TPC |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Clarity,Smoothness,High anti-blocking,Terpolymer,Low temperature heat sealing |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D792 |
| Melt Flow Rate | 7.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 44.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 850 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 830 | MPa | ASTM D747 |
| friction coefficient | |||
| With oneself – static | 0.20 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 30 | µm | |
| Secant modulus | Internal Method | ||
| MD：30 µm | 420 | MPa | Internal Method |
| TD：30 µm | 440 | MPa | Internal Method |
| Initial sealing temperature | |||
| 30 µm | 120 | ℃ | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 132 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 30 µm | 150 | ASTM D2457 | |
| Haze | |||
| 30 µm | 2.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 235 | °C | |
| Traction roller | 26 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |