| Durethan® AKV35H2.0 901510 (Dry) PA 66, 35 % glass fibers, injection molding, heat-aging stabilized&&Durethan® AKV35H2.0 901510 PA 66, 35 % glass fibers, injection molding, heat-aging stabilized&&Durethan® AKV35H2.0 901510 PA 66, 35 % glass fibers, injection molding, heat-aging stabilized&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,Heat Stabilized,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Apparent density | 0.70 | g/cm³ | ISO 60 |
| Shrinkage rate | ISO 294-4 | ||
| TD：300℃，2.0 mm | 0.91 | % | ISO 294-4 |
| TD：120℃，2.0 mm，2 hrs | 0.070 | % | ISO 294-4 |
| MD：300℃，2.0 mm | 0.37 | % | ISO 294-4 |
| MD：120℃，2.0 mm，2 hrs | 0.050 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 5.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 1.7 | % | ISO 62 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Membrane puncture strength | ISO 6603-2 | ||
| — | 3.20 | J | ISO 6603-2 |
| — | 2.60 | J | ISO 6603-2 |
| Membrane puncture force | ISO 6603-2 | ||
| — | 900 | N | ISO 6603-2 |
| — | 830 | N | ISO 6603-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 70 | kJ/m² | ISO 179/1eU |
| 23℃ | 85 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | 12 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 65 | kJ/m² | ISO 180/1U |
| 23℃ | 75 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 250 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 250 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B50 | 230 | ℃ | ISO 306 |
| B120 | 250 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 254℃ | Pass | IEC 60695-10-2 | |
| Melting temperature | 263 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD：23~55℃ | 9.0E-5 | 1/℃ | ISO 11359-2 |
| MD：23~55℃ | 3.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | |||
| 23℃ | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 23 ℃，1 mm | 35 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 23℃，100 Hz | 4.00 | IEC 60250 | |
| 23℃，1 MHz | 4.00 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 23℃，100 Hz | 0.011 | IEC 60250 | |
| 23℃，1 MHz | 0.015 | IEC 60250 | |
| Compared to the leakage tracing index | |||
| Solution A | 425 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| > 1.00 mm | 29 | ISO 3795 | |
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 600 | ℃ | IEC 60695-2-12 |
| Extreme oxygen index | 25 | % | ISO 4589-2 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | PA 66, GHR, 14-110, GF35 | ISO 1874 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 11200 | MPa | ISO 527-1-2 |
| 23℃ | 10300 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 23 ℃ | 200 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.1 | % | ISO 527-2/5 |
| Tensile Creep Modulus（1 hr） | — | MPa | ISO 899-1 |
| Tensile creep modulus | |||
| 1000 hr | — | MPa | ISO 899-1 |
| Bending modulus | |||
| 23℃ | 9300 | MPa | ASTM D790 |
| 23℃ | 10500 | MPa | ISO 178-A |
| bending strength | ASTM D790 | ||
| 23℃ | 300 | MPa | ASTM D790 |
| 5% strain, 23 ℃ | 280 | MPa | ASTM D790 |
| bending strength | |||
| 3.50% strain | 280 | MPa | ISO 178-A |
| 23℃ | 300 | MPa | ISO 178 |
| Bending strain | 4.1 | % | |
| Ball hardness | 220 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying Temperature – Dry Air Dryer | 80 | °C | |
| Drying Time – Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Residual Moisture Content | 0.030 to 0.12 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2mm, 4 hr |
| 3. 60x60x2mm, 80°C MT, 600 bar |
| 4. 0.079 in/min |
| 5. 2 mm/min |
| 6. 10°C/min |
| 7. Procedure A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |