| About |
|---|
| Flame resistant grade&& |
| Product Description | |
|---|---|
| Supplier | TEIJIN |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Low Viscosity,Good stripping performance,Flame Characteristics,High infrared light transmittance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：4.0 mm | 0.50-0.70 | % | ISO 294-4 |
| TD：4.0 mm | 0.50-0.70 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.20 | % | ISO 62 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 11.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 61.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ℃ | 6.0 | % | ISO 527-2 |
| Fracture, 23 ℃ | >50 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 2400 | MPa | ISO 527-2 |
| bending strength | |||
| 23℃ | 92.0 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 2350 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 141 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 128 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 148 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 | 1/℃ | ISO 11359-2 |
| TD | 7.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | >1.0E+15 | Ω.cm | IEC 60093 |
| Surface resistance | >1.0E+15 | Ω.cm | IEC 60093 |
| Dielectric constant | |||
| 32 | 1 kHz | IEC 60250 | |
| 3.00 | 1 MHz | IEC 60250 | |
| 3.10 | 100 HZ | IEC 60250 | |
| Dissipation factor | |||
| 1.0E-3 | IEC 60250 | ||
| 9.0E-3 | IEC 60250 | ||
| Compared to the leakage tracing index | 225 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.43 mm | V-2 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| 6.00 mm | V-0 | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 76 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | NB | kJ/m² | ISO 180/1U |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. short time test |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |