| DuPont™ Fusabond® N525 is an anhydride modified ethylene copolymer. DuPont™ Fusabond® N525 can only be used in the following applications: (1) polyamide (nylon) blends (2) blends for golf ball components (3) blends for “compatibilizing flame retardant fillers in non-halogen flame retardant polyolefin-based wire and cable compounds”&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | Ethylene copolymer |
| Material Status | Commercial: Active |
| Features | Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.880 | g/cm³ | ASTM D792 |
| Density | 0.880 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.7 | g/10min | ISO 1133 |
| 190℃，2.16kg | 3.7 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 30 | ASTM D2240 | |
| Shaw’s D | 30 | ISO 868 | |
| tensile strength | ASTM D638 | ||
| Break, 20°C 2 | 14.4 | MPa | ASTM D638 |
| Fracture, 23 ℃ | 6.43 | MPa | ASTM D638 |
| tensile strength | |||
| Break, 20°C | 14.4 | MPa | ISO 527-2/50 |
| Fracture, 23 ℃ | 6.43 | MPa | ISO 527-2/500 |
| Tensile strain | ASTM D638 | ||
| Fracture, 23 ℃ | 590 | % | ASTM D638 |
| Fracture, 23 ℃ | 550 | % | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 590 | % | ISO 527-2/50 |
| Fracture, 23 ℃ | 550 | % | ISO 527-2/500 |
| Bending modulus | |||
| 23℃ | 22.5 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -48.0 | ℃ | ASTM D3418 |
| Vicat Softening Temp | 42.0 | ℃ | ASTM D1525 |
| Vicat Softening Temp | 42.0 | ℃ | ISO 306 |
| Melting peak temperature | 53.9 | ℃ | ASTM D3418 |
| Melting temperature | |||
| DSC | 54.0 | ℃ | ISO 3146 |
| Crystallization peak temperature | |||
| DSC | 35.0 | ℃ | ASTM D3418 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Maximum Processing Temperature | 290 | ℃ |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |