| Stanyl® Diablo OCD2100 BK27021是一种聚酰胺 46（尼龙 46）材料,含有的填充物为40% 玻璃纤维增强材料。 该产品在亚太地区、北美洲或欧洲有供货,。 Stanyl® Diablo OCD2100 BK27021的主要特性为:热稳定剂。&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 46 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.0 | % | ISO 294-4 |
| MD | 0.50 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 2.2 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | ||
| — | 13000 | MPa | ISO 527-2 |
| 120℃ | 5000 | MPa | ISO 527-2 |
| 160℃ | 4600 | MPa | ISO 527-2 |
| 180℃ | 4200 | MPa | ISO 527-2 |
| 200℃ | 3400 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| fracture | 210 | MPa | ISO 527-2 |
| Fracture, 120 ℃ | 100 | MPa | ISO 527-2 |
| Fracture, 160 ℃ | 85.0 | MPa | ISO 527-2 |
| Fracture, 180 ℃ | 75.0 | MPa | ISO 527-2 |
| Fracture, 200 ℃ | 60.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| fracture | 3.0 | % | ISO 527-2 |
| Fracture, 120 ℃ | 10 | % | ISO 527-2 |
| Fracture, 160 ℃ | 11 | % | ISO 527-2 |
| Fracture, 180 ℃ | 12 | % | ISO 527-2 |
| Fracture, 200 ℃ | 13 | % | ISO 527-2 |
| Bending modulus | ISO 178 | ||
| — | 13000 | MPa | ISO 178 |
| 120℃ | 5000 | MPa | ISO 178 |
| 160℃ | 4600 | MPa | ISO 178 |
| 180℃ | 4200 | MPa | ISO 178 |
| 200℃ | 3400 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 12 | kJ/m² | ISO 179/1eA |
| 23℃ | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 65 | kJ/m² | ISO 179/1eU |
| 23℃ | 90 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 15 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 256 | ℃ | ISO 75-2/A |
| Melting temperature | 282 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 5.0E-5 | 1/℃ | ISO 11359-2 |
| MD | 2.5E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 300 | V | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Barrel rear temperature | 270 to 290 | °C | |
| Barrel middle temperature | 280 to 300 | °C | |
| Barrel front temperature | 295 to 305 | °C | |
| Nozzle temperature | 280 to 300 | °C | |
| Processing (melt) temperature | 295 to 305 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 2.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |