| Kingfa PPE-JF903是一种Polyphenylene Ether + PA 6 (PPE+Nylon 6)材料,。 该产品在北美洲或亚太地区有供货,加工方式为:注射成型。 Kingfa PPE-JF903的主要特性有: 阻燃/额定火焰 Flame Retardant 良好的尺寸稳定性 美观 无卤素 典型应用领域包括: 电气用具 工程/工业配件 |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PPO(PPE)+PA 6 |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Good Dimensional Stability,Halogen free,Flame Characteristics,Low to no phosphorus content |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 15 to 45 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.80 | % | |
| MD | 0.20 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.50 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 125 | MPa | ISO 527-2/10 |
| Tensile strain | |||
| fracture | 4.0 | % | ISO 527-2/10 |
| Bending modulus | 8000 | MPa | ISO 178 |
| bending strength | 180 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 11 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 150 | ℃ | ISO 75-2/A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.40 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 245 to 310 | °C | |
| Barrel middle temperature | 245 to 310 | °C | |
| Barrel front temperature | 245 to 310 | °C | |
| Processing (melt) temperature | 245 to 310 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection speed | 慢to中等 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |