About
Udel® P-1700 LCD polysulfone is especially well suited for the fabrication of porous membranes for filtration applications. The membranes are usually in the form of hollow fibers, but tube, plate or spiral wound forms are also used. The membranes are used in a variety of applications, such as potable water treatment, waste water treatment, blood processing, pharmaceutical purification, gas separation, dairy product processing and for processing a variety of food products. This resin offers the membrane producer good solubility in commercially available dipolar aprotic solvents, such as dimethylacetamide (DMAC), dimethylformamide, (DMF) and N-methyl pyrrolidone (NMP), which are completely miscible in water, very good control of pore size and pore size distribution, high membrane strength and good film-forming properties. Typical grades of polysulfone contain a cyclic dimer that can precipitate from solution, plugging the process filters and limiting the life of the dope solutions. Udel® P-1700 NT LCD is specially manufactured to have a lower amount of cyclic dimer. It also has a higher number average molecular weight (Mn) for a given weight average molecular weight (Mw) leading to higher fiber strength, which means fewer fiber breakages, fewer surface defects and fewer rejects. The resultant membranes have excellent hydrolytic stability and are compatible with pHs ranging from 2 to 13. They tolerate a variety of cleaning methods, including hydrochloric acid or sodium hydroxide. The resin has a Tg of 185°C indicating high thermal resistance. Transparent: Udel P-1700 NT LCD&&

About

Udel® P-1700 LCD polysulfone is especially well suited for the fabrication of porous membranes for filtration applications. The membranes are usually in the form of hollow fibers, but tube, plate or spiral wound forms are also used. The membranes are used in a variety of applications, such as potable water treatment, waste water treatment, blood processing, pharmaceutical purification, gas separation, dairy product processing and for processing a variety of food products. This resin offers the membrane producer good solubility in commercially available dipolar aprotic solvents, such as dimethylacetamide (DMAC), dimethylformamide, (DMF) and N-methyl pyrrolidone (NMP), which are completely miscible in water, very good control of pore size and pore size distribution, high membrane strength and good film-forming properties. Typical grades of polysulfone contain a cyclic dimer that can precipitate from solution, plugging the process filters and limiting the life of the dope solutions. Udel® P-1700 NT LCD is specially manufactured to have a lower amount of cyclic dimer. It also has a higher number average molecular weight (Mn) for a given weight average molecular weight (Mw) leading to higher fiber strength, which means fewer fiber breakages, fewer surface defects and fewer rejects. The resultant membranes have excellent hydrolytic stability and are compatible with pHs ranging from 2 to 13. They tolerate a variety of cleaning methods, including hydrochloric acid or sodium hydroxide. The resin has a Tg of 185°C indicating high thermal resistance. Transparent: Udel P-1700 NT LCD&&

Product Description
Supplier	Solvay
Generic	PSU
Material Status	Commercial: Active
Features	Good flexibility,Alkali resistant,Hydrolysis stability,Ethanol tolerance,Acidproof,High Heat Resistance,Solvent resistance,Hydrocarbons
Availabilitys	North America,Latin America,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.24	g/cm³	ASTM D792
Melt Flow Rate
343℃，2.16kg	6.5	g/10min	ASTM D1238
Shrinkage rate
MD	0.70	%	ASTM D955
Water absorption rate
24hr	0.30	%	ASTM D570

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	2480	MPa	ASTM D638
tensile strength	70.3	MPa	ASTM D638
Tensile strain
fracture	50 to 100	%	ASTM D638
Bending modulus	2690	MPa	ASTM D790
bending strength	106	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	69	J/m	ASTM D256
Tensile impact strength	420	kJ/m²	ASTM D1822

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	174	℃	ASTM D648
Linear coefficient of thermal expansion
MD	5.6E-5	1/℃	ASTM D696

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	5.0E+16	ohms·cm	ASTM D257
Dielectric strength	17	kV/mm	ASTM D149
Dielectric constant			ASTM D150
60 Hz	3.03		ASTM D150
1 kHz	3.04		ASTM D150
1 MHz	3.02		ASTM D150
Dissipation factor			ASTM D150
60 Hz	1.1E-3		ASTM D150
1 kHz	1.3E-3		ASTM D150
1 MHz	5.0E-3		ASTM D150

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.