| Very High Viscosity, Lubricated, Nucleated, Film Extrusion&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Nucleation,Ultra High Viscosity,Lubricating |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| friction coefficient | ISO 8295 | ||
| With oneself – dynamic, casting thin films | 0.80 | ISO 8295 | |
| Compared to itself – static, cast thin films | 1.4 | ISO 8295 | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Tensile modulus | |||
| 50 µ m, cast thin film | 465 | MPa | Internal Method |
| tensile strength | |||
| MD, yield, 50 µ m, blow molded film | 34.0 | MPa | ISO 527-3 |
| MD, 50 µ m, blow molded film | 94.0 | MPa | ISO 527-3 |
| Tensile strain | |||
| MD, fracture, 50 µ m, cast thin film | 350 | % | ISO 527-3 |
| Pant tear resistance | |||
| MD, 50 µ m, cast thin film | 32.0 | N/mm | ISO 6383-1 |
| Water vapor transmittance | |||
| 23 ℃, 85% RH, 50 µ m, cast thin film | 35 | g/m²/24 hr | DIS 15106-1/-3 |
| Oxygen transfer rate | DIS 15105-1/-2 | ||
| 0% RH：23℃，50.0 µm | 23 | cm³/m²/bar/24 hr | DIS 15105-1/-2 |
| 85% RH：23℃，50.0 µm | 33 | cm³/m²/bar/24 hr | DIS 15105-1/-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD | 9.0E-5 | 1/℃ | ISO 11359-2 |
| Specific heat capacity | |||
| — | 1550 | J/kg/℃ | |
| Average: 20 to 150 ℃ | 2250 | J/kg/℃ |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 50.0 µ m, cast thin film | 85.0 | % | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Puncture resistance | |||
| 50.0 µm | 13.2 | J/cm | Internal Method |
| RSV | 3.60 | Internal Method |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Viscosity number | 245 | cm³/g | ISO 307 |
| Apparent viscosity of melt | |||
| 260℃ | 2250 | Pa·s | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Barrel rear temperature | 230 to 235 | °C | |
| Barrel middle temperature | 235 to 250 | °C | |
| Barrel front temperature | 240 to 260 | °C | |
| Nozzle temperature | 240 to 270 | °C | |
| Processing (melt) temperature | 240 to 275 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 3.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |