| Characteristics: Moderate gel time Low viscosity Very good physical and mechanical properties after curing Filler appropriate accountability Applications: Manufacturing of mastic Manufacturing of adhesive stones&& |
| Product Description | |
|---|---|
| Generic | 热固性聚酯 |
| Material Status | Commercial: Active |
| Features | Low Viscosity |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | |||
| MD | < 1.4 | % | |
| Water absorption rate | |||
| balance | < 0.30 | % | |
| acid value | < 26.00 | mg KOH/g | |
| Gardner color | Viridescent | ||
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | < 210 | ℃ | |
| Hot deformation temperature | > 70 | ℃ |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Solid content | 60 to 64 | % | |
| viscosity | |||
| 25℃ | 0.30 to 0.45 | Pa·s | |
| Curing time | 0.067 to 0.13 | hr | |
| Gelation time | 4.0 to 9.0 | min |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Babbitt hardness | > 44 | ||
| tensile strength | > 65.0 | MPa | |
| Tensile strain | |||
| fracture | > 3.0 | % | |
| bending strength | > 120 | MPa |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Curing condition with 0.5% Co (1%) and 2% MEKP (50%) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |