| TARFLON™ MD1500是一种聚碳酸酯（PC）产品,。 它,在亚太地区有供货。 典型应用领域为:包装。 特性包括: 高纯度 快速成型周期 美观&& |
| Product Description | |
|---|---|
| Supplier | Idemitsu |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High purity,Good liquidity,Optical performance,Quick molding cycle |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 67 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.23 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 54 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 125 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 6.5E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1.6 mm | 30 | kV/mm | IEC 60243-1 |
| Dielectric constant | IEC 60250 | ||
| 100 Hz | 2.91 | IEC 60250 | |
| 1 MHz | 2.85 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 6.6E-4 | IEC 60250 | |
| 1 MHz | 9.2E-3 | IEC 60250 | |
| Arc resistance | 110 | sec | ASTM D495 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.585 | ASTM D542 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2200 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 58.0 | MPa | ISO 527-2 |
| yield | 60.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 90 | % | ISO 527-2 |
| Bending modulus | 2400 | MPa | ISO 178 |
| bending strength | 95.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 50 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 5.0 to 8.0 | hr | |
| Barrel rear temperature | 250 to 320 | °C | |
| Barrel middle temperature | 250 to 320 | °C | |
| Barrel front temperature | 250 to 320 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |