| Souleflex® SP8N-A01与 PP 有优异的接着性，具有优异的防滑性、低温柔韧性以及良好的加工性，并且易着色，可回收使用。 |
| Product Description | |
|---|---|
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Skid Resistant,Renewable resources,Soft,Good coloring |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1-10 | g/10min | ASTM D1238 |
| Shrinkage rate | 1.2-2.0 | % | — |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 80 | ASTM D2240 | |
| tensile strength | |||
| — | 8.0 | Mpa | ASTM D412 |
| 100% modulus | 3.0 | Mpa | ASTM D412 |
| 300% modulus | 4.0 | Mpa | ASTM D412 |
| Tensile strain | |||
| fracture | 540 | % | ASTM D412 |
| tear strength | 25 | KN/m | ASTM D624 |
| Compression deformation | |||
| 23℃，70 hr | 30 | % | ASTM D395B |
| 70℃，22 hr | 48 | % | ASTM D395B |
| 100℃，22 hr | 65 | % | ASTM D395B |
| Process Conditions | |||
|---|---|---|---|
| Processing temperature | Nominal value | Unit | Test method |
| Ejection temperature | |||
| Feed section | 170-190 | ℃ | |
| Middle section | 180-200 | ℃ | |
| Discharge front section | 185-205 | ℃ | |
| injector | 190-210 | ℃ | |
| maximum temperature | 250 | ℃ | |
| Injection Pressure | 高压 | ||
| injection speed | 快速 | ||
| Maintaining pressure | 不保压或底保压 | ||
| Holding time | 短 | ||
| Mold temperature | 25-40 | ℃ | |
| drying temperature | 60-80 | ℃ | |
| Drying time | 2-4 | hrs | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |