| About |
|---|
| Vydyne ECO366 is a non-halogenated, unfilled, flame-retardant PA66 homopolymer designed with superior flow properties to assist in filling thin-walled, intricate parts. It is lubricated for machine feed and easy mold release and has an Underwriters Laboratories UL 94 flammability classification of V-0 at 0.4 mm (0.016″) thick.&& |
| Product Description | |
|---|---|
| Supplier | Ascend |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Ductility,Halogen free,Good stripping performance,Flame Characteristics,Lubricating,Low density,Good tear strength,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：2.0 mm | 0.90 | % | ISO 294-4 |
| TD：2.0 mm | 0.60 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.80 | % | ISO 62 |
| 23℃，50% RH | 2.3 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 83 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 4.0 | % | ISO 527-2 |
| Poisson’s ratio | 0.40 | ISO 527-2 | |
| Tensile modulus | |||
| bending strength | |||
| 23℃ | 104 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 3900 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | 265 | ℃ | ISO 11359-2 |
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 240 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 75 | ℃ | ISO 75-2/Af |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+10 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 1.0 mm | 17 | KV/mm | IEC 60243-1 |
| Dissipation factor | |||
| Arc resistance | 120-179 | sec | IEC 61621 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.71 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Extreme oxygen index | 24 | % | ISO 4589-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 78 | kJ/m² | ISO 179/1eU |
| -30℃ | 75 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 3.7 | kJ/m² | ISO 179/1eA |
| -30℃ | 3.4 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 6.0 | kJ/m² | ISO 180-1A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4 | Hr | |
| Injection temperature | |||
| Rear barrel temperature | 260-290 | °C | |
| Central temperature of the barrel | 260-290 | °C | |
| Barrel front temperature | 260-290 | °C | |
| Die temperature | 270-285 | °C | |
| Mold temperature | 65-95 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |