| About |
|---|
| Product Description | |
|---|---|
| Supplier | Radici |
| Generic | PA66 |
| Material Status | Commercial: Negative |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 23℃ | 1.14 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃，50%RH | 2.8 | % | ISO 62 |
| melting point | |||
| 10℃/min | 262 | ℃ | ISO 3146C |
| Shrinkage rate | 1.3 | % | ISO 2577 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3100 | MPa | ISO 527 |
| tensile strength | |||
| yield | 83 | MPa | ISO 527 |
| Tensile strain | |||
| yield | 4.5 | % | ISO 527 |
| fracture | 35 | % | ISO 527 |
| bending strength | 113 | MPa | ISO 178 |
| Bending modulus | 2700 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | NB | ISO 179 | |
| Impact strength of cantilever beam notch | 5.4 | KJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 70 | ℃ | ISO 75 |
| Vicat Softening Temp | |||
| 50N | 240 | ℃ | ISO 306 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |