| NORYL™ PPX630 resin 30% GR PPE+PP. High elongation. high stiffness.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PP |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Tensile Strength,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 2.6 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.25 to 0.76 | % | Internal Method |
| MD：3.2 mm | 0.20 to 0.23 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 79.3 | MPa | ASTM D638 |
| yield | 79.3 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 7.7 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 5560 | MPa | ASTM D790 |
| bending strength | |||
| Fracture, 50 mm span | 130 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23℃ | 830 | J/m | ASTM D4812 |
| -30℃ | 100 | J/m | ASTM D256 |
| 23℃ | 170 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Total Energy | 20.4 | J | ASTM D3763 |
| 23℃，Total Energy | 19.1 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 134 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 155 | ℃ | ASTM D648 |
| Vicat Softening Temp | 162 | ℃ | ASTM D1525 4 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 7.7E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 1.4E-5 | 1/℃ | ASTM E831 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 66 to 77 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 243 to 288 | °C | |
| Barrel middle temperature | 249 to 288 | °C | |
| Barrel front temperature | 254 to 293 | °C | |
| Nozzle temperature | 260 to 299 | °C | |
| Processing (melt) temperature | 260 to 299 | °C | |
| Mold temperature | 38 to 66 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.051 to 0.076 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |