| About |
|---|
| PETROTHENE M2520 is a film grade resin that exhibits excellent optics, good gloss, good bubble stability and outstanding processability. A typical application for this resin is high clarity packaging that requires higher modulus.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Good surface appearance,Smoothness,Optical performance,High anti-blocking,Food contact compliance |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.925 | g/cm³ | ASTM D1558 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Secant modulus | |||
| 1% secant, TD, 25 µ m, blow molded film | 338 | MPa | ASTM D882 |
| 1% secant, MD, 25 µ m, blow molded film | 269 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture, 25 µ m, blow molded film | 22.8 | MPa | ASTM D882 |
| TD, yield, 25 µ m, blow molded film | 13.1 | MPa | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 29.6 | MPa | ASTM D882 |
| MD, yield, 25 µ m, blow molded film | 11.7 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 25 µ m, blow molded film | 470 | % | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 130 | % | ASTM D882 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 75 | g | ASTM D1709 |
| tear strength | |||
| TD, 25 µ m, blow molded film | 80 | g | ASTM D1922 |
| MD, 25 µ m, blow molded film | 270 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25.4 µ m, blow molded film | 70 | ASTM D2457 | |
| Haze | |||
| 25.4 µ m, blow molded film | 5.5 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |