DIC.PPS AMORVON® WL-30

About
Outline: WL-30 is a glass fiber and poly tetra fluoro ethylene filled modified PPS compound that provides low friction and wear resistance. Color: Black&&

Product Description
SupplierDIC Corporation
GenericPPS
Material StatusCommercial: Active
FeaturesLow coefficient of friction,Good wear resistance,V-0
AvailabilitysNorth America,Asia Pacific
Process MethodsInjection Molding

Technical Data
PHYSICALNominal valueUnitTest method
Density1.68g/cm³ASTM D792
Shrinkage rate ASTM D955
MD0.25%ASTM D955
TD1.0%ASTM D955
Water absorption rate
23℃,24hr0.050%ASTM D570

IMPACTNominal valueUnitTest method
Impact strength of cantilever beam notch60J/mASTM D256
Notched impact strength of cantilever beam350J/mASTM D256

THERMALNominal valueUnitTest method
Hot deformation temperature
1.8 MPa, unannealed230ASTM D648
Linear coefficient of thermal expansion ASTM D696
MD:-30~90℃2.3E-51/℃ASTM D696
TD:-30~90℃2.3E-51/℃ASTM D696

Electrical performanceNominal valueUnitTest method
Volume resistivity1.0E+16ohms·cmASTM D257
Dielectric strength
1.6 mm16kV/mmASTM D149
Dielectric constant
1 MHz4.00 ASTM D150
Dissipation factor
1 MHz2.0E-3 ASTM D150
Arc resistance120secASTM D495

FLAME CHARACTERISTICSNominal valueUnitTest method
0.80 mmV-0 UL 94

MECHANICALNominal valueUnitTest method
Rockwell hardness ASTM D785
M-level98 ASTM D785
R-level118 ASTM D785
Tensile modulus10000MPaASTM D638
tensile strength150MPaASTM D638
Tensile strain
fracture1.6%ASTM D638
Bending modulus9000MPaASTM D790
bending strength200MPaASTM D790
compressive strength170MPaASTM D695
Poisson’s ratio0.36 
friction coefficient ASTM D1894
Steel – Dynamic0.22 ASTM D1894
Steel – Static0.23 ASTM D1894
Elongation at break and bending2.0%ASTM D790

Process Conditions
injectionNominal valueUnitTest method
Barrel rear temperature290 to 320°C
Barrel middle temperature290 to 320°C
Barrel front temperature290 to 320°C
Mold temperature120 to 150°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.