| NAS® 36 is a styrene acrylic copolymer that can be used in a variety of applications demanding a strong, stiff water-clear plastic resin with excellent thermal and indoor UV light stability. FEATURES Sparkling clarity Indoor UV light stability Low density Ease of processing Enhanced mold release APPLICATIONS Point of purchase displays Office accessories Appliances Toys Appliances&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | SMMA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Excellent Processability,Good Clarity,Good stripping performance,Low density,Copolymer,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ASTM D792 |
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 2.2 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 220℃，10 kg | 30.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.20 to 0.60 | % | ISO 294-4 |
| MD | 0.20 to 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.15 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 0.15 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 1.5 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 12 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 2.5 | kJ/m² | ISO 180-A |
| 23℃ | 21 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | 12 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 80.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 90.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 104 | ℃ | ASTM D1525 3 |
| B50 | 98.0 | ℃ | ISO 306 |
| Maximum operating temperature | 260 | ℃ |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.560 | ASTM D542 | |
| Refractive index | 1.560 | ISO 489 | |
| Transmittance | |||
| 550 nm | 91.4 | % | ASTM D1003 |
| Haze | 0.30 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3240 | MPa | ASTM D638 |
| Tensile modulus | 3300 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 60.0 | MPa | ISO 527-2 |
| Yield, 23 ℃ | 60.7 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.5 | % | ISO 527-2 |
| fracture | 2.3 | % | ASTM D638 |
| Bending modulus | 3170 | MPa | ASTM D790 |
| Bending modulus | 3400 | MPa | ISO 178 |
| bending strength | 101 | MPa | ASTM D790 |
| bending strength | 100 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 75 | ASTM D785 | |
| Ball hardness | 169 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Barrel rear temperature | 180 to 210 | °C | |
| Barrel middle temperature | 200 to 230 | °C | |
| Barrel front temperature | 210 to 240 | °C | |
| Processing (melt) temperature | 200 to 240 | °C | |
| Mold temperature | 30 to 60 | °C | |
| Injection speed | Slow-Moderate | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4h/80°C |
| 3. Rate B (120°C/h), Loading 1 (10 N) |
| 4. Sodium D Line |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |