| About |
|---|
| Versaflex™ CE 3620 is targeted for consumer electronics applications where abrasion resistance, UV resistance and enhanced feel are required. Versaflex™ CE 3620 can also overmold to a variety of substrates including PC,ABS, PC/ABS and Copolyester.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Sprayable,Low coefficient of friction,Good wear resistance,Solvent resistance,Good coloring,HB |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shore A, 10 seconds | 65 | ASTM D2240 | |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| fracture | 7.03 | MPa | ASTM D412 |
| 100% strain | 3.05 | MPa | ASTM D412 |
| 300% strain | 4.26 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 630 | % | ASTM D412 |
| tear strength | 40.6 | kN/m | ASTM D624 |
| Compression deformation | |||
| 23℃，22 hr | 18 | % | ASTM D395 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.5 to 13.0 mm, All Colors | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Common material types | 苯乙烯类热塑性弹性体 (TES |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 0.998 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 2.0 to 15 | g/10min | ASTM D1238 |
| 200℃，5.0kg | 25 to 35 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 1.1 to 1.7 | % | ASTM D955 |
| Apparent viscosity of melt | |||
| 200℃ | 19.4 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 52 to 60 | °C | |
| Drying time | 1.0 to 3.0 | hr | |
| Recommended maximum moisture content | 0.020 to 0.030 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 171 to 182 | °C | |
| Barrel middle temperature | 182 to 221 | °C | |
| Barrel front temperature | 188 to 227 | °C | |
| Nozzle temperature | 193 to 238 | °C | |
| Processing (melt) temperature | 193 to 232 | °C | |
| Mold temperature | 13 to 43 | °C | |
| Back pressure | 0.00 to 0.345 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Notes |
|---|
| 1. Please contact GLS Thermoplastic Elastomers for a copy of the compliance letter. PolyOne Corporation does not approve the use of this product in any application classified as medical device, drug packaging or any other application in contact with drugs/pharmaceuticals. |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. Die C |
| 4. 2 hr |
| 5. 25% deflection |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |