| XUS 58710实验聚烯烃弹性体是乙烯-辛烯共聚物，具有良好的流量特性，具有非常广泛的通用型热塑性弹性体的应用。US 58710实验提供所需的聚烯烃弹性体共混物的冲击性能与聚丙烯（PP）和聚乙烯（PE）。xus58710.00提供高填充能力和良好的过氧化物固化能力。当过氧化物、硅烷或辐射交联时，它具有良好的耐热老化性、压缩性和耐候性，可用于生产高性能的电绝缘材料。 |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.870 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| Mooney viscosity | 24 | MU | ASTM D1646 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -52.0 | ℃ | Internal Method |
| Vicat Softening Temp | 45.0 | ℃ | ASTM D1525 |
| Melting temperature | 60.0 | ℃ | Internal Method |
| Crystallization peak temperature | 45.0 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 100% secant | 2.90 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 9.76 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 810 | % | ASTM D638 |
| Bending modulus | |||
| 2% secant | 13.1 | MPa | ASTM D790 |
| 1% secant | 14.3 | MPa | ASTM D790 |
| Tensile strength | 40 | kN/m | ASTM D624 |
| Shore A, 1 second | 73 | ASTM D2240 | |
| Shore D, 1 second | 22 | ASTM D2240 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |