| Polyetherimide reinforced with Glass fiber and PTFE for use in Burn-in Test Sockets (BiTS) Application&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Lubricating |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | ASTM D792, ISO 1183 |
| Shrinkage rate | Internal Method | ||
| MD | 0.40 | % | |
| TD | 0.52 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 8630 | MPa | ASTM D638 |
| — | 8550 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 157 | MPa | ASTM D638 |
| fracture | 156 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| fracture | 1.2 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 6420 | MPa | ASTM D790 |
| — | 7220 | MPa | ISO 178 |
| bending strength | ASTM D790 | ||
| Yield, 50 mm span | 202 | MPa | |
| Fracture, 50 mm span | 201 | MPa | |
| friction coefficient | |||
| With oneself – dynamic | 0.52 | ASTM D3702 | |
| Wear factor | |||
| Washer | 15.6 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 67 | J/m | ASTM D256 |
| 23℃ | 7.8 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 330 | J/m | ASTM D4812 |
| 23℃ | 26 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 204 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 207 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 1.4E-5 | 1/℃ | |
| TD：-40~40℃ | 5.1E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 2.0E+13 | ohms | ASTM D257 |
| Volume resistivity | 7.6E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1.6 mm in oil | 31 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 100 kHz | 3.30 | ASTM D150 | |
| Dissipation factor | |||
| 100 kHz | 3.1E-3 | ASTM D150 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 149 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 24 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |