| PRODUCT DESCRIPTION: SABIC® LDPE HPO823N is a Low Density Polyethylene grade without slip and anti-block additives. It typically exhibits good melt strength and processability. Films typically exhibit good toughness, heat seal, optics and has good biaxial shrink properties. TYPICAL APPLICATIONS: Shrink film, lamination film, bags & pouches. This product is not intended for use in medical and pharmaceutical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,Good heat sealing,Optical performance,Food contact compliance,Good melt strength,Low density |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 0.05 mm | 260 | MPa | ISO 527-2 |
| friction coefficient | > 80 | % | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| film thickness | 25 – 100 micron | ||
| tensile strength | ISO 527-3 | ||
| Yield, 0.05 mm | 11.0 | MPa | ISO 527-2 |
| MD, fracture, 50 µ m, blow molded film | 26.0 | MPa | |
| TD, fracture, 50 µ m, blow molded film | 24.0 | MPa | |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 50 µ m, blow molded film | 300 | % | |
| TD, fracture, 50 µ m, blow molded film | 600 | % | |
| Drop hammer impact | |||
| 50 µ m, blow molded film | 150 | g | ASTM D1709 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 96.0 | ℃ | ISO 306/A50 |
| Melting temperature | |||
| DSC | 111 | ℃ | ISO 3146 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | ASTM D2457 | ||
| 20 °, 50 µ m, blow molded film | > 40 | ||
| 60 °, 50.0 µ m, blow molded film | > 90 | ||
| Haze | |||
| 50 µ m, blow molded film | < 8.0 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blow（up Ratio） | 2.50 to 4.00 | ||
| memo_intro |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 170 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |