| About |
|---|
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Halogen free |
| Availabilitys | Europe,Asia Pacific,Africa & Middle East |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.38 | g/cm³ | ISO 1183/A |
| Shrinkage rate | |||
| TD | 1.0 | % | |
| MD | 0.30 | % | |
| Water absorption rate | |||
| 23℃，24hr | 1.2 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 1.8 | % | ISO 1110 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 9600 | MPa | ISO 527-2-1A |
| tensile strength | |||
| Fracture, 23 ℃ | 140 | MPa | ISO 527-2-1A |
| Fracture, 23 ℃ | 130 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ASTM D638 |
| Fracture, 23 ℃ | 2.8 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 8300 | MPa | ASTM D790 |
| 23℃ | 7700 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 220 | MPa | ISO 178 |
| Fracture, 23 ℃ | 200 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃ | 95 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 6.8 | kJ/m² | ISO 180 |
| Charpy Notched Impact Strength | |||
| 23℃ | 9.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 65 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 246 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 260 | ℃ | ASTM D648 |
| Melting temperature | 258 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 0.01E+15 | ohms·cm | IEC 60093 |
| Surface resistivity | 1.0E+14 | ohms | IEC 60093 |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80 mm | V-0 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 0.80 mm | 960 | ℃ | IEC 60695-2-12 |
| 1.6 mm | 960 | ℃ | IEC 60695-2-12 |
| 3.2 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 0.8 mm | 750 | ℃ | IEC 60695-2-13 |
| 1.6 mm | 775 | ℃ | IEC 60695-2-13 |
| 3.2 mm | 775 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Recommended maximum moisture content | 0.20 | % | |
| Temperature at the rear of the barrel | 265 to 275 | °C | |
| Temperature in the middle of the barrel | 265 to 275 | °C | |
| Front temperature of material barrel | 270 to 280 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |