| About |
|---|
| Abstron SE-22M是一种丙烯腈丁二烯苯乙烯(ABS)产品,。 它可以通过片材挤出成型或型材挤出成型进行加工,在亚太地区有供货。 典型应用领域为:薄板。 主要特性为:阻燃/额定火焰。&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 8.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.50 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 3.2mm | 450 | J/m | |
| 6.4mm | 350 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 94.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 107 | ℃ | ASTM D1525 2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 107 | ASTM D785 | |
| tensile strength | |||
| Yield, 3.20 mm | 40.2 | MPa | ASTM D638 |
| Bending modulus | |||
| 6.40 mm | 1910 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 6.40 mm | 54.9 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 85.0 to 90.0 | °C | |
| Drying time | 3.0 to 3.5 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Barrel 1 zone temperature | 210 to 250 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |