| About |
|---|
| A rigid ceramic-reinforced composite with excellent thermal, moisture and abrasion resistance. Applications Heat and wear resistant components Stiff/Rigid assemblies and prototypes Composite Ceramic-like components Aesthetic components for art and archival models Moisture stable components Automotive and aerospace applications Features A plastic-ceramic composite High thermal resistance Excellent abrasion resistance Moisture resistant Extremely rigid Benefits Aesthetically beautiful white parts Withstand temperatures of up to 220°C Models that can withstand wear in aggressive applications Components can survive in adverse thermal environments Components can be plated Parts retain properties & dimensions for extended durations&& |
| Product Description | |
|---|---|
| Generic | 3D打印材料 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,Good Dimensional Stability,High Heat Resistance,Moisture resistance,Good wear resistance,Electroplating |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.59 | g/cm³ | |
| — | 1.62 | g/cm³ | |
| viscosity | |||
| 30℃ | 1.50 to 2.00 | Pa·s | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 15 to 18 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 148 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 220 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 95.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 97.0 | ℃ | ASTM D648 |
| Glass transition temperature | DMA | ||
| — | 108 to 110 | ℃ | DMA |
| — | 112 to 114 | ℃ | DMA |
| Linear coefficient of thermal expansion | |||
| MD | ASTM E831 | ||
| 25 to 57 ℃ | 3.1E-5 | cm/cm/℃ | ASTM E831 |
| 70 to 200 ℃ | 8.7E-5 | cm/cm/℃ | ASTM E831 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Critical Exposure | 7.20 | mJ/cm² | |
| Penetration depth | 144.8 | µm |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 89 | ||
| Tensile modulus | 9460 to 9680 | MPa | ASTM D638 |
| tensile strength | 78.0 to 87.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.0 to 1.5 | % | ASTM D638 |
| Bending modulus | 8270 to 8370 | MPa | ASTM D790 |
| bending strength | 137 to 145 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Liquid, 25°C |
| 3. Solid, 25°C |
| 4. Thermal Postcure 2 hr @ 120 °C |
| 5. Thermal Postcure @ 120 °C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |