| An accurate print material for jewelry and fine featured pattern production Applications Jewelry manufacturing Direct casting Master pattern production Models requiring high detail Features Outstanding accuracy 0.025mm layer thickness capability Low ash formulation Benefits Fine features are faithfully reproduced Easy feature visualization Material can be burned out for direct casting&& |
| Product Description | |
|---|---|
| Generic | 3D打印材料 |
| Material Status | Commercial: Active |
| Features | Good surface appearance |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.10 | g/cm³ | |
| — | 1.18 | g/cm³ | |
| viscosity | |||
| 30℃ | 0.16 to 0.2 | Pa·s | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 29 to 40 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 38.0 | ℃ | |
| 1.8 MPa, unannealed | 33.0 | ℃ | |
| Glass transition temperature | 58.0 | ℃ | DSC |
| Linear coefficient of thermal expansion | |||
| MD | ASTM E831 | ||
| 25 to 50 ℃ | 1.4E-4 | cm/cm/℃ | |
| 75 to 140 ℃ | 1.7E-4 | cm/cm/℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Critical Exposure | 8.23 | mJ/cm² | |
| Penetration depth | 73.7 | µm |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 72 | ||
| Tensile modulus | 910 to 1110 | MPa | ASTM D638 |
| tensile strength | 20.0 to 24.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 9.0 to 16 | % | ASTM D638 |
| Bending modulus | 1080 to 1420 | MPa | ASTM D790 |
| bending strength | 28.0 to 38.0 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Liquid, 25°C |
| 3. Solid, 25°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |