| About |
|---|
| Aclam® TC100 is a low temperature heat sealable lamination composed of a 2 mil (50µ) polyolefin heat seal layer and a 4 mil (100µ) proprietary Aclar® 11C film layer.&& |
| Product Description | |
|---|---|
| Supplier | Honeywell |
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Active |
| Features | Good heat sealing |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| friction coefficient | ASTM D1894 | ||
| &Metal – Dynamic | 0.43 | ||
| Metal – Static | 0.55 | ||
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | ASTM D882 | ||
| MD：51 µm | 1000 | MPa | |
| TD：51 µm | 965 | MPa | |
| tensile strength | ASTM D882 | ||
| MD, yield, 51 µ m | 38.6 | MPa | |
| TD, yield, 51 µ m | 27.6 | MPa | |
| Tensile strain | ASTM D882 | ||
| MD, yield, 51 µ m | 230 | % | |
| TD, yield, 51 µ m | 150 | % | |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：51 µm | 500 | g | |
| TD：51 µm | 1600 | g | |
| Oxygen permeability | |||
| 23℃，51 µm，0% RH | 0.79 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water vapor transmittance | ASTM F1249 | ||
| 50℃，90% RH | 0.26 | g·mm/m²/atm/24 hr | |
| 38℃，100% RH | 0.062 | g·mm/m²/atm/24 hr |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |