| About |
|---|
| Aclar 33C (0.75 mil) is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It is thermoformable on both pressure and vacuum forming machines.&& |
| Product Description | |
|---|---|
| Supplier | Honeywell |
| Generic | PCTFE |
| Material Status | Commercial: Active |
| Features | Copolymer |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.12 | g/cm³ | ASTM D1505 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | ASTM D882 | ||
| MD：19 µm | 1660 | MPa | ASTM D882 |
| TD：19 µm | 1450 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 19 µ m | 83.0 | MPa | ASTM D882 |
| TD, yield, 19 µ m | 27.6 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, yield, 19 µ m | 100 | % | ASTM D882 |
| TD, yield, 19 µ m | 100 | % | ASTM D882 |
| Water vapor transmittance | |||
| 19 µm，38℃，100% RH | 0.42 | g·mm/m²/atm/24 hr | ASTM F1249 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Crystallization peak temperature | |||
| DSC | 206 | ℃ | ASTM D3418 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 19.1 µm | < 1.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |