| About |
|---|
| Aclar SupRx 900 is a 0.90 mil CTFE homopolymer high performance barrier film for the pharmaceutical and medical markets. It thermoforms well on conventional blister packaging equipment and offers improved barrier over 22A at a competitive cost.&& |
| Product Description | |
|---|---|
| Supplier | Honeywell |
| Generic | PCTFE |
| Material Status | Commercial: Active |
| Features | Block resin,Homopolymer |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.11 | g/cm³ | ASTM D1505 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | ASTM D882 | ||
| MD：23 µm | 1380 | MPa | ASTM D882 |
| TD：23 µm | 1290 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 23 µ m | 109 | MPa | ASTM D882 |
| TD, yield, 23 µ m | 51.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, yield, 23 µ m | 100 | % | ASTM D882 |
| TD, yield, 23 µ m | 250 | % | ASTM D882 |
| Water vapor transmittance | ASTM F1249 | ||
| 23 µm，25℃，60% RH | 0.034 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 23 µm，30℃，60% RH | 0.056 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 23 µm，40℃，75% RH | 0.23 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 23 µm，38℃，100% RH | 0.26 | g·mm/m²/atm/24 hr | ASTM F1249 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 22.9 µm | < 1.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |