| Acryft® CM8014 is an Ethylene Methyl Methacrylate (EMMA) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America.&& |
| Product Description | |
|---|---|
| Supplier | Sumitomo |
| Generic | EMMA |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | JIS K7112 |
| Melt Flow Rate | 4.0 | g/10min | JIS K7210 |
| ESCR(Environmental Stress Cracking Resistance) | > 300 | hr | ASTM D1693 |
| MMA Content | 17.5 | wt% | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -75.0 | ℃ | JIS K7216 |
| Vicat Softening Temp | 60.0 | ℃ | JIS K7206 |
| Melting temperature | 79.0 to 110 | ℃ | JIS K7121 |
| Ring and Ball Softening Point | 170 | ℃ | JIS K2207 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 91 | ||
| Shaw’s D | 36 | ||
| tensile strength | |||
| fracture | 10.0 | MPa | JIS K7113 |
| Tensile strain | |||
| fracture | 700 | % | JIS K7113 |
| Bending modulus | |||
| 23℃ | 32.0 | MPa | ASTM D747 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |