ACRYLITE® Hi-Gloss FT15

About
ACRYLITE® Hi-Gloss FT15 polymer is an amorphous thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA). ACRYLITE® Hi-Gloss FT15 polymer is available in a range of opaque colors including deep jet black. Typical properties of ACRYLITE® Hi-Gloss acrylic polymers are: excellent weather resistance high light transmission high mechanical strength high surface hardness and mar resistance good melt flow rate versatile colorability due to crystal clarity The special properties of ACRYLITE® Hi-Gloss FT15 polymer are: high heat resistance available in transparent and a range of opaque colors medium melt flow rate AMECA listed Application: Used for injection molding and extrusion applications.&&

About

ACRYLITE® Hi-Gloss FT15 polymer is an amorphous thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA). ACRYLITE® Hi-Gloss FT15 polymer is available in a range of opaque colors including deep jet black. Typical properties of ACRYLITE® Hi-Gloss acrylic polymers are: excellent weather resistance high light transmission high mechanical strength high surface hardness and mar resistance good melt flow rate versatile colorability due to crystal clarity The special properties of ACRYLITE® Hi-Gloss FT15 polymer are: high heat resistance available in transparent and a range of opaque colors medium melt flow rate AMECA listed Application: Used for injection molding and extrusion applications.&&

Product Description
Supplier	ROHM
Generic	PMMA
Material Status	Commercial: Active
Features	Good Rigidity,Weather resistance is good,Good Clarity,Good liquidity,Good Hardness,High Heat Resistance,High scratch resistance,Good coloring,Amorphous
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.19	g/cm³	ISO 1183
Melt Volume Rate
230℃，3.8 kg	4.50	cm³/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	3500	MPa	ISO 527-1-2
tensile strength
fracture	50.0	MPa	ISO 527-2/5
Tensile strain
fracture	3.1	%	ISO 527-2/5

IMPACT	Nominal value	Unit	Test method
Charpy Unnotch Impact strength
23℃	18	kJ/m²	ISO 179/1eU

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	105	℃	ISO 75-2/A
0.45 MPa, unannealed	107	℃	ISO 75-2/B
Glass transition temperature	121	℃	IEC 1006
Vicat Softening Temp
B50	115	℃	ISO 306

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Igniting temperature of the hot wire	675	℃	IEC 60695-2-13
Flame retardant level	B2		DIN 4102

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.