ACRYLITE® LED 8N LD96

About
ACRYLITE® LED 8N LD96 Acrylic Molding Compound is a highly transparent light guide material based on ACRYLITE® 8N. In addition to the typical properties of ACRYLITE®, such as Excellent weather resistance UV-stability Good flow, high mechanical strength ACRYLITE® LED 8N LD96 is developed for edge lit LED applications. The light scattering properties convert the light guide to a full illuminated panel. Furthermore, the material allows for a competely transparent view through the light guide when it is not illuminated. This opens a new degree of freedom for designers. ACRYLITE® 8N LD12 is recommended for panels with a distance of 48 cm to 96 cm between two light injecting LED strips. Application: Injection molding or extrusion.&&

About

ACRYLITE® LED 8N LD96 Acrylic Molding Compound is a highly transparent light guide material based on ACRYLITE® 8N. In addition to the typical properties of ACRYLITE®, such as Excellent weather resistance UV-stability Good flow, high mechanical strength ACRYLITE® LED 8N LD96 is developed for edge lit LED applications. The light scattering properties convert the light guide to a full illuminated panel. Furthermore, the material allows for a competely transparent view through the light guide when it is not illuminated. This opens a new degree of freedom for designers. ACRYLITE® 8N LD12 is recommended for panels with a distance of 48 cm to 96 cm between two light injecting LED strips. Application: Injection molding or extrusion.&&

Product Description
Supplier	ROHM
Generic	PMMA
Material Status	Commercial: Active
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.19	g/cm³	ASTM D792
Apparent density	0.66	g/cm³	ASTM D1895
Melt Flow Rate
230℃，3.80kg	3.3	g/10min	ASTM D1238
Shrinkage rate
MD	0.40 to 0.70	%	ASTM D955
Water absorption rate
balance	< 0.30	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃，6.4mm	19	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, annealed, 6.35 mm	100	℃	ASTM D648
Vicat Softening Temp	108	℃	ASTM D1525
Linear coefficient of thermal expansion
MD：0~100℃	7.2E-5	1/℃	ASTM D696

optical performance	Nominal value	Unit	Test method
Transmittance
3200 µm	92.0	%	ASTM D1003
Haze
3200 µm	< 1.0	%	ASTM D1003
Yellowness index
3.20 mm	< 1.0	YI	ASTM D1925

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	3240	MPa	ASTM D638
tensile strength	77.9	MPa	ASTM D638
Tensile strain
fracture	4.0 to 6.0	%	ASTM D638
yield	4.0 to 6.0	%	ASTM D638
Bending modulus	3450	MPa	ASTM D790
bending strength	112	MPa	ASTM D790
Rockwell hardness
M-level	95		ASTM D785

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.