| ACRYLITE® Resist ZK6SR polymer is an amorphous, impact-modified thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA). Typical properties of ACRYLITE® Resist acrylic polymers are: high weather resistance high light transmission improved resistance to stress cracking good melt flow rate easy to color The special properties of ACRYLITE® Resist ZK6SR polymer are: high impact/break resistance and strength high melt strength for extrusion low melt flow rate medium heat resistance AMECA listed as ZK6 (x) Application: Used for extruded sheet, co-extruded sheet and extruded profiles.&& |
| Product Description | |
|---|---|
| Supplier | ROHM |
| Generic | PMMA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Good Clarity,Low liquidity,High impact resistance,Good melt strength,Heat Resistance, Good,Good coloring,Amorphous |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ASTM D792 |
| Apparent density | 0.71 | g/cm³ | ASTM D1895 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 1.3 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| balance | < 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 0℃，6.4mm | 43 | J/m | ASTM D256 |
| 23℃，3.2mm | 59 | J/m | ASTM D256 |
| 23℃，6.4mm | 59 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed, 6.35 mm | 82.8 | ℃ | ASTM D648 |
| Vicat Softening Temp | 91.1 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | |||
| MD：0~100℃ | 9.0E-5 | 1/℃ | ASTM D696 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 3200 µm | > 90.0 | % | ASTM D1003 |
| Haze | |||
| 3200 µm | < 2.0 | % | ASTM D1003 |
| Yellowness index | |||
| 3.20 mm | 0.20 | YI | ASTM D1925 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1590 | MPa | ASTM D638 |
| tensile strength | 41.4 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 60 | % | ASTM D638 |
| yield | 5.0 | % | ASTM D638 |
| Bending modulus | 1380 | MPa | ASTM D790 |
| bending strength | 55.2 | MPa | ASTM D790 |
| Rockwell hardness | |||
| M-level | 40 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |