| About |
|---|
| ACRYPET® IR S404 is a Polymethyl Methacrylate Acrylic material. It is available in Asia Pacific or North America. Important attributes of ACRYPET® IR S404 are: Impact Modified UV Stabilized&& |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | PMMA |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 8.5 | g/10min | ISO 1133 |
| Spiral flow length | Internal Method | ||
| — | 23.0 | cm | Internal Method |
| — | 33.0 | cm | Internal Method |
| Shrinkage rate | 0.30 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.30 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.6 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 49 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | 3.7 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 85.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 88.0 | ℃ | ISO 306/B |
| Linear coefficient of thermal expansion | |||
| MD | 9.0E-5 | 1/℃ | ASTM D696 |
| specific heat | 1500 | J/kg/℃ | JIS K7123 |
| Thermal conductivity coefficient | 0.20 | W/m/K | ASTM C177 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+16 | ohms | JIS K6911 |
| Volume resistivity | > 1.0E+15 | ohms·cm | JIS K6911 |
| Dielectric strength | 20 | kV/mm | JIS K6911 |
| Dielectric constant | |||
| 60 Hz | 3.70 | JIS K6911 | |
| Dissipation factor | |||
| 60 Hz | 0.050 | JIS K6911 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.490 | ASTM D542 | |
| Transmittance | |||
| Total, 3000 µ m | 92.0 | % | ISO 13468 |
| Haze | |||
| 3000 µm | 0.50 | % | ISO 14782 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1800 | MPa | ISO 527-2/1A/1 |
| tensile strength | 53.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 40 | % | ISO 527-2/1A/5 |
| Bending modulus | 1900 | MPa | ISO 178 |
| bending strength | 76.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 70 | ISO 2039-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Melt Temperature: 446°F |
| 3. Melt Temperature: 482°F |
| 4. 4000 V/sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |